- 常用金属牌号及硬度
- 帖子创建时间：2011-08-11 评论：1 浏览：886
-
牌号 C Si Mn P S Ni Cr Mo Cu N 其它 备注 中国 日本 1Cr17Mn6Ni5N SUS201 ≦0.15 ≦1.0 5.5~7.5 ≦0.06 ≦0.03 3.5~5.5 16.0~18.0 - - ≦0.25 1Cr18Mn8Ni5N SUS202 ≦0.15 ≦1.0 7.5~10.00 ≦0.06 ≦0.03 4.0~6.0 17.0~19.0 - - 1Cr17Ni7 SUS301 0.15~0.25 ≦1.0 ≦2.0 ≦0.035 ≦0.03 6.0~8.0 16.0~18.0 - - - 1Cr18Ni9 SUS302 ≦0.15 ≦1.0 ≦2.0 ≦0.035 ≦0.03 8.0~10.0 17.0~19.0 - - - 1Cr18Ni9Si3 SUS302B ≦0.15 2.0~3.0 ≦2.0 ≦0.035 ≦0.03 8.0~10.0 17.0~19.0 - - - 0Cr19Ni9 SUS304 ≦0.07 ≦1.0 ≦2.0 ≦0.035 ≦0.03 8.0~10.0 17.0~19.0 - - - 00Cr19Ni10 SUS304L ≦0.03 ≦1.0 ≦2.0 ≦0.035 ≦0.03 8.0~12.0 18.0~20.0 - - - 0Cr19Ni9N SUS304NI ≦0.08 ≦1.0 ≦2.5 ≦0.035 ≦0.03 7.0~10.5 18.0~20.0 - - - 00Cr12 SUS401L ≦0.03 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.0~13.5 - - - 1Cr17 SUS430 ≦0.12 ≦0.75 ≦1.0 ≦0.035 ≦0.03 - 16.0~18.0 - - - 1Cr17Mo SUS434 ≦0.12 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 16.0~18.0 0.75~1.35 - - 00Cr17Mo SUS436L ≦0.025 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 17.0~20.0 0.75~1.35 - ≦0.25 00Cr18Mo2 SUS444 ≦0.025 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.5~13.5 1.75~2.5 - ≦0.25 Ti、Zr等*少 1Cr13 SUS410 ≦0.15 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.5~13.5 - - - 0Cr13 SUS410S ≦0.08 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.5~13.5 - - - 1Cr17Ni2 SUS431 0.11~0.17 ≦0.8 ≦0.8 ≦0.035 ≦0.03 1.5~2.5 16.0~18.0 - - - 2Cr25Ni20 SUS310 ≦0.25 ≦1.5 ≦2.0 ≦0.035 ≦0.03 19.0~22.0 24.0~26.0 - - - 0Cr25Ni20 SUS310S ≦0.08 ≦1.5 ≦2.0 ≦0.035 ≦0.03 19.0~22.0 24.0~26.0 - - - 0Cr23Ni13 SUS309S ≦0.08 ≦1.5 ≦1.5 ≦0.035 ≦0.03 12.0~14.0 22.0~24.0 - - - 1Cr25Ni20Si2 SUS310S ≦0.20 1.5~2.5 ≦1.5 ≦0.035 ≦0.03 18.0~21.0 24.0~27.0 - - - 00Cr18Ni11 SUS3042B ≦0.03 ≦1.0 ≦2.0 ≦0.035 ≦0.03 9.0~12.0 17.0~20.0 - - - 15#/15F - ≦0.1 - ≦0.5 ≦0.035 ≦0.025 - - - - - Al<0.1 优质碳钢 10#/10F - ≦0.08 - ≦0.045 ≦0.035 ≦0.025 - - - - - Al<0.05 冲压用碳钢 08#/08F/Al - ≦0.01 - ≦0.040 ≦0.025 - - - - - - - 深冲用碳钢 常用金属材料化学成份 常用金属材料化学成份 牌号 C Si Mn P S Ni Cr Mo Cu N 其它 备注 中国 日本 BUFD - ≦0.008 - ≦0.3 ≦0.02 - - - - - - *薄通用碳钢 BSUFD - ≦0.006 - ≦0.3 ≦0.02 - - - - - - 1Cr15Mn8Ni15Cu2N 201Cu 0.11~0.17 ≦0.88 ≦0.8 ≦0.035 ≦0.03 4.5~5.5 14.0~16.0 - 1.5~2.5 - 0Cr13Ni2Mn12Cu2 200Cu ≦0.08 ≦1.5 11.0~13.0 ≦0.035 ≦0.03 1.5~2.5 12.0~14.0 - 1.5~2.5 - 常用铜及铜合金化学成分 中国牌号 日本牌号 Cu+Ag P Ag Bi Sb Zn Fe Pb 备注 T1 C1100 99.95 0.001 / 0.001 0.002 0.005 0.005 0.003 1号纯铜 T2 C1020 99.9 / / 0.001 0.002 / 0.005 0.005 2号纯铜 T3 C1100BB 99.7 / / 0.002 / / / 0.01 3号纯铜 TU0 C1020 99.9 0.0003 0.0025 0.0001 0.0004 0.0001 0.001 0.0005 0号无氧铜 TU1 C1020BD 99.97 0.002 / 0.001 0.002 0.003 0.004 0.004 1号无氧铜 TU2 99.95 0.002 / 0.001 0.002 0.003 0.004 0.004 2号无氧铜 TP1 C1201 99.9 0.004~0.012 / / / / / / 1号脱磷铜 TP2 C1221 99.9 0.015~0.040 / / / / / / 2号脱磷铜 TAg0.1 99.50 / 0.05~0.12 0.002 0.005 / 0.05 0.01 0.1银铜 H96 C2100/C2200 95.0~97.0 / / / Ni0.5 余量 0.1 0.03 低锌黄铜 H59 C2600 57.0~59.0 / / / Ni0.5 余量 0.3 0.5 普通黄铜 HFe59-1-1 C3560 57.0~60.0 Al0.1~0.2 Mn0.5~0.8 Sn0.3~0.7 Ni0.5 余量 0.6~1.2 0.2 铁黄铜 QBe1.9-0.1 C1700 余量 Be1.85~2.1 Ni0.2~0.4 / / Ti0.10~0.25 0.15 0.005 铍青铜 QSn8-0.3 C52100 余量 0.03~0.35 Sn7.0~9.0 / Ni0.2 0.2 0.1 0.05 锡青铜 QMn5 C5210 余量 / Mn4.5~5.5 0.1 0.002 / 0.35 0.03 锰青铜 HPb62-0.8 C4621 60.0~63.0 / / / Ni0.5 余量 0.2 0.5~1.2 铅黄铜 HPb59-1 C4430 57.0~60.0 / / / Ni1.0 余量 0.5 0.8~1.9 铅黄铜 HMn57-3-1 C6711 55~58 Mn2.5-3.5 Al 0.5~1.5 / Ni0.5 余量 1.0 0.2 锰黄铜 HSn60-1 C4250 59~61 / Sn1.0~1.5 / Ni0.5 余量 0.1 0.3 锡黄铜 QSn4-0.3 C51100 余量 ≦0. 35 Sn3.5~4.9 / Ni0.2 0.3 0.1 0.05 锡青铜 QSn1.5-0.2 C50500 余量 0.03~0.35 Sn1.0~1.7 / Ni0.2 0.3 0.1 0.05 锡青铜 QAl C61000 余量 Al 60~8.5 / Ni 0.5 Si 0.1 0.2 0.5 0.02 铝青铜 QCr1 C18200 余量 Cr 0.6~1.2 Si 0.1 / / / / / 铬青铜 QFe2.5 C19400 97.0 0.015~0.15 / / / 0.05~0.2 2.1~2.6 0.03 常用铝及铝合金化学成份表 中国牌号 日本牌号 Cu Si Mg Mn Ni Fe Zn 备注 LA30 A1N30 0.05 0.1~0.2 0.01 0.01 0.01 LA50 A1N50 0.1 0.3 0.05 3A21 A3003 0.2 0.6 1.0~1.6 0.05 ZL102 ADC1 10.0~13.0 ZL301 AC7B 9.5~11.0 ZL105 AC4D 1.0~1.5 4.5~5.5 0.4~0.6 ZL203 AC1A 4.0~4.5 6.5~7.5 ZA1Si7MgZL101 AC4C 6.5~7.5 0.25~0.45 Ti 0.08~0.2 ZL101A AC4CH 0.25~0.45 注：该化学成分中，除标明含金属元素外，其余均为铝！ 硬度是衡量材料软硬程度的一个性能指标。硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。*常用的是静负荷压入法硬度试验，即布氏硬度HB、洛氏硬度HRA，HRB，HRC、维氏硬度HV，橡胶塑料邵氏硬度HA,HD等硬度其值表示材料表面抵抗坚硬物体压入的能力。而里氏硬度Hl、肖氏硬度HS则属于回跳法硬度试验，其值代表金属弹性变形功的大小。因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。 1.HRC含意是洛式硬度C标尺， 2.HRC和HB在生产中的应用都很广泛 3.HRC适用范围HRC 20－－67，相当于HB225－－650 若硬度**此范围则用洛式硬度A标尺HRA。 若硬度低于此范围则用洛式硬度B标尺HRB。 布式硬度上限值HB650,不能**此值。 4.洛氏硬度计C标尺之压头为*角120度的金刚石圆锥，试验载荷为一确定值，中国标准是150公斤力。 布氏硬度计之压头为淬硬钢球HBS或硬质合金球HBW，试验载荷随球直径不同而不同，从3000到31.25公斤力。 5.洛式硬度压痕很小，测量值有局部性，须测数点求平均值，适用成品和薄片，归于无损检测一类。 布式硬度压痕较大，测量值准，不适用成品和薄片，一般不归于无损检测一类。 6.洛式硬度的硬度值是一无名数，没有单位。因此习惯称洛式硬度为多少度是不正确的。 布式硬度的硬度值有单位，且和抗拉强度有一定的近似关系。 7.洛式硬度直接在表盘上显示、也可以数字显示，操作方便，快捷直观，适用于大量生产中。 布式硬度需要用显微镜测量压痕直径，然后查表或计算，操作较繁琐。 8.在一定条件下，HB与HRC可以查表互换。 硬度试验是机械性能试验中*简单易行的一种试验方法。为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。 实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
- 文章标签：
-
快速评论您好，您还未登录，暂时还不能评价，请先登录
-
yfn8888 2011-08-11楼 0踩 0赞 回复 引用
牌号 C Si Mn P S Ni Cr Mo Cu N 其它 备注 中国 日本 1Cr17Mn6Ni5N SUS201 ≦0.15 ≦1.0 5.5~7.5 ≦0.06 ≦0.03 3.5~5.5 16.0~18.0 - - ≦0.25 1Cr18Mn8Ni5N SUS202 ≦0.15 ≦1.0 7.5~10.00 ≦0.06 ≦0.03 4.0~6.0 17.0~19.0 - - 1Cr17Ni7 SUS301 0.15~0.25 ≦1.0 ≦2.0 ≦0.035 ≦0.03 6.0~8.0 16.0~18.0 - - - 1Cr18Ni9 SUS302 ≦0.15 ≦1.0 ≦2.0 ≦0.035 ≦0.03 8.0~10.0 17.0~19.0 - - - 1Cr18Ni9Si3 SUS302B ≦0.15 2.0~3.0 ≦2.0 ≦0.035 ≦0.03 8.0~10.0 17.0~19.0 - - - 0Cr19Ni9 SUS304 ≦0.07 ≦1.0 ≦2.0 ≦0.035 ≦0.03 8.0~10.0 17.0~19.0 - - - 00Cr19Ni10 SUS304L ≦0.03 ≦1.0 ≦2.0 ≦0.035 ≦0.03 8.0~12.0 18.0~20.0 - - - 0Cr19Ni9N SUS304NI ≦0.08 ≦1.0 ≦2.5 ≦0.035 ≦0.03 7.0~10.5 18.0~20.0 - - - 00Cr12 SUS401L ≦0.03 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.0~13.5 - - - 1Cr17 SUS430 ≦0.12 ≦0.75 ≦1.0 ≦0.035 ≦0.03 - 16.0~18.0 - - - 1Cr17Mo SUS434 ≦0.12 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 16.0~18.0 0.75~1.35 - - 00Cr17Mo SUS436L ≦0.025 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 17.0~20.0 0.75~1.35 - ≦0.25 00Cr18Mo2 SUS444 ≦0.025 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.5~13.5 1.75~2.5 - ≦0.25 Ti、Zr等*少 1Cr13 SUS410 ≦0.15 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.5~13.5 - - - 0Cr13 SUS410S ≦0.08 ≦1.0 ≦1.0 ≦0.035 ≦0.03 - 11.5~13.5 - - - 1Cr17Ni2 SUS431 0.11~0.17 ≦0.8 ≦0.8 ≦0.035 ≦0.03 1.5~2.5 16.0~18.0 - - - 2Cr25Ni20 SUS310 ≦0.25 ≦1.5 ≦2.0 ≦0.035 ≦0.03 19.0~22.0 24.0~26.0 - - - 0Cr25Ni20 SUS310S ≦0.08 ≦1.5 ≦2.0 ≦0.035 ≦0.03 19.0~22.0 24.0~26.0 - - - 0Cr23Ni13 SUS309S ≦0.08 ≦1.5 ≦1.5 ≦0.035 ≦0.03 12.0~14.0 22.0~24.0 - - - 1Cr25Ni20Si2 SUS310S ≦0.20 1.5~2.5 ≦1.5 ≦0.035 ≦0.03 18.0~21.0 24.0~27.0 - - - 00Cr18Ni11 SUS3042B ≦0.03 ≦1.0 ≦2.0 ≦0.035 ≦0.03 9.0~12.0 17.0~20.0 - - - 15#/15F - ≦0.1 - ≦0.5 ≦0.035 ≦0.025 - - - - - Al<0.1 优质碳钢 10#/10F - ≦0.08 - ≦0.045 ≦0.035 ≦0.025 - - - - - Al<0.05 冲压用碳钢 08#/08F/Al - ≦0.01 - ≦0.040 ≦0.025 - - - - - - - 深冲用碳钢 常用金属材料化学成份 常用金属材料化学成份 牌号 C Si Mn P S Ni Cr Mo Cu N 其它 备注 中国 日本 BUFD - ≦0.008 - ≦0.3 ≦0.02 - - - - - - *薄通用碳钢 BSUFD - ≦0.006 - ≦0.3 ≦0.02 - - - - - - 1Cr15Mn8Ni15Cu2N 201Cu 0.11~0.17 ≦0.88 ≦0.8 ≦0.035 ≦0.03 4.5~5.5 14.0~16.0 - 1.5~2.5 - 0Cr13Ni2Mn12Cu2 200Cu ≦0.08 ≦1.5 11.0~13.0 ≦0.035 ≦0.03 1.5~2.5 12.0~14.0 - 1.5~2.5 - 常用铜及铜合金化学成分 中国牌号 日本牌号 Cu+Ag P Ag Bi Sb Zn Fe Pb 备注 T1 C1100 99.95 0.001 / 0.001 0.002 0.005 0.005 0.003 1号纯铜 T2 C1020 99.9 / / 0.001 0.002 / 0.005 0.005 2号纯铜 T3 C1100BB 99.7 / / 0.002 / / / 0.01 3号纯铜 TU0 C1020 99.9 0.0003 0.0025 0.0001 0.0004 0.0001 0.001 0.0005 0号无氧铜 TU1 C1020BD 99.97 0.002 / 0.001 0.002 0.003 0.004 0.004 1号无氧铜 TU2 99.95 0.002 / 0.001 0.002 0.003 0.004 0.004 2号无氧铜 TP1 C1201 99.9 0.004~0.012 / / / / / / 1号脱磷铜 TP2 C1221 99.9 0.015~0.040 / / / / / / 2号脱磷铜 TAg0.1 99.50 / 0.05~0.12 0.002 0.005 / 0.05 0.01 0.1银铜 H96 C2100/C2200 95.0~97.0 / / / Ni0.5 余量 0.1 0.03 低锌黄铜 H59 C2600 57.0~59.0 / / / Ni0.5 余量 0.3 0.5 普通黄铜 HFe59-1-1 C3560 57.0~60.0 Al0.1~0.2 Mn0.5~0.8 Sn0.3~0.7 Ni0.5 余量 0.6~1.2 0.2 铁黄铜 QBe1.9-0.1 C1700 余量 Be1.85~2.1 Ni0.2~0.4 / / Ti0.10~0.25 0.15 0.005 铍青铜 QSn8-0.3 C52100 余量 0.03~0.35 Sn7.0~9.0 / Ni0.2 0.2 0.1 0.05 锡青铜 QMn5 C5210 余量 / Mn4.5~5.5 0.1 0.002 / 0.35 0.03 锰青铜 HPb62-0.8 C4621 60.0~63.0 / / / Ni0.5 余量 0.2 0.5~1.2 铅黄铜 HPb59-1 C4430 57.0~60.0 / / / Ni1.0 余量 0.5 0.8~1.9 铅黄铜 HMn57-3-1 C6711 55~58 Mn2.5-3.5 Al 0.5~1.5 / Ni0.5 余量 1.0 0.2 锰黄铜 HSn60-1 C4250 59~61 / Sn1.0~1.5 / Ni0.5 余量 0.1 0.3 锡黄铜 QSn4-0.3 C51100 余量 ≦0. 35 Sn3.5~4.9 / Ni0.2 0.3 0.1 0.05 锡青铜 QSn1.5-0.2 C50500 余量 0.03~0.35 Sn1.0~1.7 / Ni0.2 0.3 0.1 0.05 锡青铜 QAl C61000 余量 Al 60~8.5 / Ni 0.5 Si 0.1 0.2 0.5 0.02 铝青铜 QCr1 C18200 余量 Cr 0.6~1.2 Si 0.1 / / / / / 铬青铜 QFe2.5 C19400 97.0 0.015~0.15 / / / 0.05~0.2 2.1~2.6 0.03 常用铝及铝合金化学成份表 中国牌号 日本牌号 Cu Si Mg Mn Ni Fe Zn 备注 LA30 A1N30 0.05 0.1~0.2 0.01 0.01 0.01 LA50 A1N50 0.1 0.3 0.05 3A21 A3003 0.2 0.6 1.0~1.6 0.05 ZL102 ADC1 10.0~13.0 ZL301 AC7B 9.5~11.0 ZL105 AC4D 1.0~1.5 4.5~5.5 0.4~0.6 ZL203 AC1A 4.0~4.5 6.5~7.5 ZA1Si7MgZL101 AC4C 6.5~7.5 0.25~0.45 Ti 0.08~0.2 ZL101A AC4CH 0.25~0.45 注：该化学成分中，除标明含金属元素外，其余均为铝！ 硬度是衡量材料软硬程度的一个性能指标。硬度试验的方法较多，原理也不相同，测得的硬度值和含义也不完全一样。*常用的是静负荷压入法硬度试验，即布氏硬度HB、洛氏硬度HRA，HRB，HRC、维氏硬度HV，橡胶塑料邵氏硬度HA,HD等硬度其值表示材料表面抵抗坚硬物体压入的能力。而里氏硬度Hl、肖氏硬度HS则属于回跳法硬度试验，其值代表金属弹性变形功的大小。因此，硬度不是一个单纯的物理量，而是反映材料的弹性、塑性、强度和韧性等的一种综合性能指标。 1.HRC含意是洛式硬度C标尺， 2.HRC和HB在生产中的应用都很广泛 3.HRC适用范围HRC 20－－67，相当于HB225－－650 若硬度**此范围则用洛式硬度A标尺HRA。 若硬度低于此范围则用洛式硬度B标尺HRB。 布式硬度上限值HB650,不能**此值。 4.洛氏硬度计C标尺之压头为*角120度的金刚石圆锥，试验载荷为一确定值，中国标准是150公斤力。 布氏硬度计之压头为淬硬钢球HBS或硬质合金球HBW，试验载荷随球直径不同而不同，从3000到31.25公斤力。 5.洛式硬度压痕很小，测量值有局部性，须测数点求平均值，适用成品和薄片，归于无损检测一类。 布式硬度压痕较大，测量值准，不适用成品和薄片，一般不归于无损检测一类。 6.洛式硬度的硬度值是一无名数，没有单位。因此习惯称洛式硬度为多少度是不正确的。 布式硬度的硬度值有单位，且和抗拉强度有一定的近似关系。 7.洛式硬度直接在表盘上显示、也可以数字显示，操作方便，快捷直观，适用于大量生产中。 布式硬度需要用显微镜测量压痕直径，然后查表或计算，操作较繁琐。 8.在一定条件下，HB与HRC可以查表互换。 硬度试验是机械性能试验中*简单易行的一种试验方法。为了能用硬度试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。 实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越高，塑性变形抗力越高，硬度值也就越高。
- 0
成员 - 1
信息数 - 申请加入
- 圈公告
- 圈资料
圈主:
yfn8888- 圈子成立时间：2016-07-05
- 圈主商铺：
http://yfn8888.cn.b2b168.com
yfn8888
- 成功加入的圈子
共1条 1页 1